2-component epoxy resin adhesive
50 ml double cartridge, black, clear Weicon Easy-Mix HT 180Item-no.: 1324771Supplier number: 10044884EAN: 4024596067021
PU (Packaging): 6 STKQuantity:
1 STKPackable
Description
WEICON Easy-Mix HT 180 is a 2-component adhesive based on epoxy resin with high temperature resistance up to +180°C (+356°F), short-term up to +230°C (+446°F). The adhesive is highly viscous and stable which also makes it suitable for vertical applications. It is impact- and shock-resistant, has a long pot life, cures at room temperature and is machinable after curing. The adhesive is particularly suitable for the bonding of composite materials and metal and can be spot-welded while curing. Easy-Mix HT 180 can also be used on plastics, ceramics, glass, stone or wood and is suitable for adhesions where larger tolerances have to be bridged. Due to special fillers, it is possible to achieve a non-varying and reliable adhesive joint of at least 0.20 - 0.25 mm. The high temperature resistance enables the bonding of components, which are thermo-coated (powder-coated) after curing.
Attributes
Aluminium sandblasted
13 N/mm²
Base
Epoxy resin, mineral-filled
Bending strength |DIN EN ISO 178
46.0 MPa
CFRP
22.0 N/mm²
Colour
black
Compressive strength|DIN EN ISO 604
52.0 MPa
Consistency
pasty, gap-filling
Construction material class|DIN 4102
B2
Curing temperature
+10 °C - +50 °C
Density of the mixture
1,1 g/cm³
Dielectric strength|DIN EN 60243-1 (20°C)
18 kV/mm
E-modulus (tensile)|DIN EN ISO 527-2
2.300 - 2.700 MPa
End hardness|(100 % of strength)
24 Hours
Gap bridging up to max.
4 mm
Hardness (Shore D)|DIN ISO 7619
80
Manual strength|(35 % of strength)
120 Min.
Mechanically loadable after|(50 % of strength)
4 Hours
Mixing ratio by weight
2:1
PVC-hard roughened
11.0 N/mm²
Processing temperature
+10 °C to +40 °C °C
Sales bundle
Cartridge
Shrinkage
0,3 %
Stainless steel V2A sandblasted
24.0 N/mm²
Steel 1.0338 sandblasted
23.0 N/mm²
Temperature conductivity
0.172 mm²/s
Temperature resistance
-50 °C to 180 °C briefly up to +230 °C
Tensile strength|DIN EN ISO 527-2
27.0 MPa
Tg after curing at RT|(DSC)
54,4 °C
Tg after tempering (at 120 °C)|(DSC)
44,7 °C
Thermal capacity|DIN EN ISO 22007-4
1.335 J/(g·K)
Thermal conductivity|DIN EN ISO 22007-4
0.26 W/m·K
Through resistance|DIN EN 62631-3-1
2,48 · 10¹¹ Ω·m
Viscosity of the mixture
pasty