MS polymer-based adhesive
310 ml cartridge, white, silicone-free Weicon Flex 310 M ClassicItem-no.: 1123568Supplier number: 10002576EAN: 4024596001186
PU (Packaging): 12 STKQuantity:
1 STKPackable
Item available in 5 variants:
Description
WEICON Flex 310 M Classic is strong, paintable (wet-on-wet), sandable, has an outstanding resistance to ageing and good resistance to UV rays. It is resistant to fresh and salt water and is free of silicone, isocyanate, halogens and solvents. The product as an ISEGA certificate and can be used as an adhesive in the food technology. Flex 310 M Classic is an elastic adhesive based on MS polymer and is suitable for the bonding of metals, many plastics, ceramics, wood, glass and stone. This adhesive and sealant can be used in metal construction, tank and apparatus engineering, carriage, vehicle and container construction, ventilation and air conditioning systems, in the electrical industry, yacht and boat construction, and in all applications where silicones or products containing silicones are not suitable.
Attributes
Average tensile shear strength (DIN EN 1465/ASTM D 1002)
2.1 N/mm²
Base
1 K. polyoxypropylene
Colour
white
Composition
pasty
Construction material class|DIN 4102
B 2
Density|(+20°C) DIN 51757
1,44 g/cm³
Elongation at break (tensile)|DIN 53504/ASTM D412
650 %
Gap bridging up to max.
5 mm
Hardening method
moisture-curing
Hardness (Shore A)|DIN ISO 7619
42±5
Hardness condition
+5 to +40°C and 30% to 95% relative humidity
Max. sealing joint width
25.0 mm
Processing temperature
+5°C to +40°C °C
Sales bundle
Cartridge
Skin forming time
25 Min.
Specific resistance
> 10^10 Ω·cm
Stability/run-off | ASTM D 2202
1.0 mm
Tear resistance | DIN 53515 / ASTM D 1002
20.0 kN/m
Temperature resistance
-40°C to +90°C short term up to +130°C
Tensile strength of the pure adhesive and sealant |ISO 37
3.3 N/mm²
Tensile strength|ISO 37 / S3A
3.3 N/mm²
Tg after curing at RT
~ -55 °C
Through resistance|2.3 mm layer thickness
1,0 x 10^10 Ω·m
Through-hardening speed|in the first 24 hours
2 - 3 mm
Tracking resistance|DIN EN 60112
CTI 800
Volume change|DIN 52451
-1 %