Zinc spray
400 ml spray can, special light colour WeiconItem-no.: 1122668Supplier number: 10000047EAN: 4024596000387
PU (Packaging): 12 STKQuantity:
1 STKPackable
Description
WEICON Zinc Spray "bright grade" is approved by the German TÜV and provides all metal surfaces with a long-lasting cathodic corrosion protection. It has a bright colour shade matching fresh hot-dip galvanization. It forms a fast-drying, adherent protective layer of microfine zinc flakes. The zinc flakes form a resistant protective layer even against extreme weather and environmental conditions. Even after more than 550 hours in the salt spray test according to DIN EN 9227, metal parts coated with WEICON Zinc Spray "bright grade" did not show any corrosion. WEICON Zinc Spray "bright grade" can be used for the coating of welded joints and drill holes, as a conductive intermediate layer for spot welding and wherever metal must be protected against corrosion.
Attributes
Abrasion resistant
ja
Binding agent
Modified alkyd resin
Colour shade
Matched to fresh hot-dip galvanising
Construction material class|DIN 4102
B2
Consumption|at 1.5 cross pass
150 ml/m²
Density|(+20°C) DIN 51757
1,0 g/cm³
Double nozzle
No
Dust dry according to
15 Min.
Grating section|DIN 53151/ISO 2409
Cross-sectional characteristic GT 0 to GT 1
Layer thickness with 1.5 cross pass approx.
30 - 50 μm
Mandrel bending test|DIN EN ISO 1519
No hairline cracking
Metal content in the dry film
~70 %
Overcoatable
after 24 Hours
Pigment
platelet-shaped zinc and aluminium pigments
Pigment purity
approx. 99.9% Zn / approx. 99.5% Al
Processing temperature
+5 °C to +35 °C, optimum +18 °C to +35 °C °C
Recommended primer
Zinc spray
Sales bundle
Spray can
Temperature resistance
-50 °C to +300 °C
Top coat
not required